Zinc Aluminum Spray is an active means of cathodic corrosion protection. The resistant, flexible, heat-resistant zinc film which is produced protects iron and steel components from rust and corrosion. Zinc Aluminum Spray can also be used as the only means of corrosion protection.
- can be painted over
- outstanding corrosion protection
- high zinc content
- smooth, pore-free film
- outstanding thermal stability
- electrically conductive
Density at 20 °C: 0,79 g/cm³
Zinc purity: > 99 %
Propellant: propane, butane
Drying time: 5-7 min. dust dry, 20-30 min. touch dry, can be painted over after 8 hours
Proportion of zinc: > 99 % (as a dry film) %
Binder: special resins
Operating temperature range: up to 250 °C
Form: aerosol, liquid
Flash point: < 0 °C
Areas of application
Used to protect iron and steel components from rust and corrosion. Suitable for repairing all damaged forms of galvanising (hot-dip, flame spraying and electroplated zinc). Zinc Aluminum Spray can also be used as the only means of weather-resistant corrosion protection.
Shake can vigorously for at least 1 minute before use. Spray onto clean, dry, degreased metallic surfaces. Can be painted over after 8 hours. Layer thickness of the zinc film dry after a single spraying: 25-35 µm.
After use, clear spray nozzle by inverting can and spraying until only the propellant emerges.